Shenzhen Bluewind Vermiculite Products Co., Ltd. sales01@bluewindvp.com 86-0755-83251674
Product Details
Place of Origin: Shenzhen, China
Brand Name: Bluewind
Model Number: V-1200
Payment & Shipping Terms
Minimum Order Quantity: 600 pieces
Price: $3.65/pieces 600-2999 pieces
Packaging Details: Fumigation free pallet with wrapping film, and hardboard angle protecting.
Size 1025*635*1160 mm per pallet, 22 pcs* 15 layers * 65 mm per pallet, and 32 pallets per 20 GP
Delivery Time: 15workdays
Supply Ability: 100000 Piece/Pieces per Month
Shape: |
Brick |
Material: |
Vermiculite Brick, Exfoliated Vermiculite |
SiO2 Content (%): |
48-55 % |
Al2O3 Content (%): |
12-16% |
MgO Content (%): |
12-16% |
CaO Content (%): |
2-4% |
Refractoriness (Degree): |
Common (1580°< Refractoriness< 1770°) |
CrO Content (%): |
0 |
SiC Content (%): |
0 |
Processing Service: |
Punching, Cutting, Moulding |
Size: |
230*114*65mm |
Bulk Density G/cm3: |
1.2 |
Usage: |
Furnace Liner |
Keyword: |
Acid Proof Silica Refractory Bricks |
APPARENT POROSITY: |
70-72 |
Cold Crush Strength: |
9.5 Mpa |
Bend Strength: |
3.5 Mpa |
Refractoriness / C: |
1200 C |
Thermal Conductivity(w/mk): |
<0.28 |
Port: |
Tianjin Port |
Shape: |
Brick |
Material: |
Vermiculite Brick, Exfoliated Vermiculite |
SiO2 Content (%): |
48-55 % |
Al2O3 Content (%): |
12-16% |
MgO Content (%): |
12-16% |
CaO Content (%): |
2-4% |
Refractoriness (Degree): |
Common (1580°< Refractoriness< 1770°) |
CrO Content (%): |
0 |
SiC Content (%): |
0 |
Processing Service: |
Punching, Cutting, Moulding |
Size: |
230*114*65mm |
Bulk Density G/cm3: |
1.2 |
Usage: |
Furnace Liner |
Keyword: |
Acid Proof Silica Refractory Bricks |
APPARENT POROSITY: |
70-72 |
Cold Crush Strength: |
9.5 Mpa |
Bend Strength: |
3.5 Mpa |
Refractoriness / C: |
1200 C |
Thermal Conductivity(w/mk): |
<0.28 |
Port: |
Tianjin Port |
Physical parameter
|
|
|
|
|||
Density (kgs/m3)
|
700
|
800
|
900
|
|||
Max temp.
|
1150 ℃
|
1150 ℃
|
1150 ℃
|
|||
Strength
|
4.5/2.0 MPa
|
5.5/2.1 MPa
|
6.2/2.2 MPa
|
|||
Linear shrinkage
|
1%
|
1%
|
1%
|
|||
Thermal conduct.
|
|
|
|
|||
@ 200 ℃
|
0.14 W/m.k
|
0.16 W/m.k
|
0.18 W/m.k
|
|||
@ 400 ℃
|
0.16W/m.k
|
0.18 W/m.k
|
0.2 W/m.k
|
|||
@ 600 ℃
|
0.18 W/m.k
|
0.2 W/m.k
|
0.22 W/m.k
|
|||
Chemical parameter
|
|
|
|
|||
SiO2
|
43-46 %
|
43-46 %
|
45-48 %
|
|||
Al2O3
|
10-13 %
|
10-13 %
|
13-16 %
|
|||
Fe2O3
|
4-6 %
|
4-6 %
|
4-6 %
|
|||
TiO
|
1-2 %
|
1-2 %
|
1-2 %
|
|||
MgO
|
16-23 %
|
16-23 %
|
14-20 %
|
|||
K2O
|
7-10 %
|
7-10 %
|
5-8 %
|
|||
Na2O
|
1-2 %
|
1-2 %
|
1-2 %
|
|||
LOI @ 1000 C
|
4-6 %
|
4-6 %
|
3-5 %
|
|||
Standard size & Thickness
|
|
|
|
|||
1005*615 mm
|
10-60 mm thickness
|
10-60 mm thickness
|
10-60 mm thickness
|
|||
1225*615 mm
|
10-60 mm thickness
|
10-60 mm thickness
|
10-60 mm thickness
|